In the third generation of solar cells, cheaper absorbent layers such as Cu2ZnSnS4 (CZTS) have been developed with specifications similar to Cu2InGaS4 (CIGS). This CZTS material is known as a material with good structural and optical properties where the CZTS material has a series of atoms bonded to each other to form a kesterite or stannite crystal arrangement. In its use as an absorbent layer for solar cells, CZTS material is synthesized using the electrochemical deposition method. In this electrochemical deposition technique, an electrical circuit will be connected to the electrode and inserted into the electrolyte. Several voltage variations from 1 volt to 5 volts will be applied to the electrical circuit, which will then trigger ions from the precipitating material in the electrolyte to stick to one of the electrodes. Variation of deposition voltage was carried out to determine the effect of deposition stress on the electrochemical deposition method on the characteristics of the CZTS absorbent layer. The characterizations used are X-Ray Diffraction (XRD), UV-Vis Spectrometry, and I-V meter. XRD results show that the resulting crystal size is getting smaller with greater deposition voltage around 6.07 - 7.27 nm. The optical absorption results show that the CZTS absorber layer is sensitive at low wavelengths around 300 – 480 m,, with Light Harvesting Efficiency (LHE) ranging from 13.3 - 24.75%. The band gap energy values obtained ranged from 1.4 to 1.48 eV. The cell efficiency test results show an excellent efficiency value according to the reference ranges from 2.56-8.77%. These results indicate that the deposition voltage affects the characteristics of the CZTS absorbent layer for solar cell applications.
Full-Text [PDF 839 kb]
(1561 Downloads)
Highlights
- Cu2ZnSnS4 thin film layer was fabricated by the electrochemical deposition method
- Voltage variation results in the kesterite band gap from 1.40-1.48 eV
- Solar cell performs an excellent efficiency of 8.77% via the non-vacuum process