Iranian Journal of Materials Science and Engineering

---

Mono dispersed nano SiC particles with spherical morphology were synthesized in this project by hydrolysis and condensation mechanism during sol gel processing. pH, temperature and precursor’s ratio considered as the main parameters which could influence particles size. According to DLS test results, the smallest size of particles in the sol (<5nm) was obtained at pH<4. It can be observed from rheology test results optimum temperature for achieving nanometeric gel is about 60 ˚C. The optimum pH values for sol stabilization was (2-5) determined by zeta potentiometery. Si 29NMR analysis was used in order to get more details on final structure of gel powders resulted from initial sol. X-ray diffraction studies showed sythesized powder consists of β-SiC phase. Scanning electron microscopy indicated agglomerates size in β-SiC synthesis is less than 100 nm. Finally, TEM studies revealed morphology of β-SiC particles treated in 1500˚C and after 1hr aging is spherical with (20-30) nm size

---

Vanadium recovery of Thermal Power Plant Ash (TPPA) is an attractive process which simultaneously satisfies the pollution control standards regarding TPPA disposal and provides a valuable source of vanadium for industrial demands. In the present research work, sulfuric acid leaching route has been employed for vanadium recovery from an Iranian TPPA. Effects of acid concentration, temperature, acid/TPPA ratio, leaching time as well as TPPA particle size on the leaching efficiency of vanadium have been investigated. Experimental results showed that leaching efficiency of vanadium is significantly affected by the leaching conditions. The results revealed that with acid concentration of about 15%, temperature around 75 °C, acid/TPPA ratio~15, leaching time about 120 minutes and particle size of 75 - 150 pm, almost 92% of vanadium can be dissolved

---

Variation in microstructural features of 2024 aluminum alloy plastically deformed by equal channel angular pressing (ECAP) at room temperature, was investigated by X-Ray diffraction in this work. These include dislocation density dislocation characteristic and the cell size of crystalline domains. Dislocations contrast factor was calculated using elastic constants of the alloy such as C 11, C 22 and C 44 . The effect of dislocations contrast factor on the anisotropic strain broadening of diffraction profiles was considered for measuring the microstructural features on the base of the modified Williamson-Hall and Warren-Averbach methods. Results showed that the dislocations density of the solution annealed sample increased from 4.28×10 12m-2 to 2.41×10 14m-2 after one pass of cold ECAP and the fraction of edge dislocations in the solution annealed sample increased from 43% to 74% after deformation. This means that deformation changed the overall dislocations characteristic more to edge dislocations. Also the crystalline cell size of the solution annealed sample decreased from 0.83μm to about 210nm after one pass of ECAP process at room temperature

---

Short banana fiber reinforced composites have been prepared in laboratory to determine mechanical properties. It has been observed that as soon as the percentage of the banana fiber increases slightly there is a tremendous increase in ultimate tensile strength, % of strain and young modulus of elasticity. Reinforcement of banana fibers in epoxy resin increases stiffness and decreases damping properties of the composites. Therefore, 2.468% banana fiber reinforced composite plate stabilizes early as compared to 7.7135 % banana fiber reinforced composite plate but less stiff as compared to 7.7135 % banana fiber reinforced composite plate

---

The presence of alloying elements, sometimes in a very small amount, affects mechanical properties one of these elements is Boron. In Aluminum industries, Boron master alloy is widely used as a grain refiner In this research, the production process of Aluminum –Boron master alloy was studied at first then, it was concurrently added to 2024 Aluminum alloy. After rolling and homogenizing the resulting alloy, the optimal temperature and time of aging were determined during the precipitation hardening heat treatment by controlled quenching (T6C). Then, in order to find the effect of controlled quenching, different cycles of heat treatment including precipitation heat treatment by controlled quenching (T6C) and conventional quenching (T6) were applied on the alloy at the aging temperature of 110°C. Mechanical properties of the resulting alloy were evaluated after aging at optimum temperature of 110°C by performing mechanical tests including hardness and tensile tests. The results of hardness test showed that applying the controlled quenching instead of conventional quenching in precipitation heat treatment caused reduction in the time of reaching the maximum hardness and also increase in hardness rate due to the generated thermo-elastic stresses rather than hydrostatic stresses and increased atomic diffusion coefficient as well. Tensile test results demonstrated that, due to the presence of boride particles in the microstructure of the present alloy, the ultimate tensile strength in the specimens containing Boron additive increased by 3.40% in comparison with the specimens without such an additive and elongation (percentage of relative length increase) which approximately increased by 38.80% due to the role of Boron in the increase of alloy ductility

---

Accumulative roll-bonding process (ARB) is an important severe plastic deformation technique for production of the ultrafine grained, nanostructured and nanocomposite materials in the form of plates and sheets. In the present work, this process used for manufacturing Al/SiO 2 nanocomposites by using Aluminum 1050 alloy sheets and nano sized SiO 2 particles, at ambient temperature. After 8 cycles of ARB process, the tribological properties and wear resistance of produced nanocomposites were investigated. The wear tests by abrasion were performed in a pinon-disc tribometer. Results show that by increasing ARB cycles and the amount of nano powders, the friction coefficient of produced nanocomposites decreases.

---

Microstructure and corrosion performance of admiralty brass (ADB) and aluminum brass (ALB) alloys after passing different annealing heat treatments were investigated using optical and scanning electron microscope, energy dispersive X-ray spectroscopy (EDS), X-ray diffraction (XRD), DC polarization measurements and electrochemical impedance spectroscopy (EIS). The results showed that heat treating of ALB caused gradient in aluminum concentration across the grains whose increased with increasing of annealing temperature. On the other hand, corrosion current density (i corr) of ADB in 3.5%NaCl media decreased with increasing of recrystallization, while ALB showed corrosion behavior inconsistent with ADB. The impedance measurements showed that corrosion rate of ADB decreased with increasing of exposure time from 0 to 15 days which could be related to the formation of SnO 2 surface film and the Sn-rich phases. While polarization resistance of ALB decreased by passing days in the corrosive media which could be associated to establishing of differential aluminum concentration cells.

---

This article examines the Weibull statistical analysis that was used for investigating the effect of melt filtration on tensile properties and defects formed inside the casting. Forming and entrapping of double oxide films have been explained by using the context of critical velocity of melt in the runner. SutCast software results were used to examine the amounts of the velocity of melt as such. SEM/EDX analysis is used to observe the presence of double oxide films in the fracture surfaces of the tensile specimens. The article goes on to propose that castings made with foam filters with smaller pores show higher mechanical properties and reliability due to higher Weibull modulus and fewer defects

---

In this research accumulative roll bonding process as sever plastic deformation process was applied up to 8 cycles to produce the ultrafine grain copper. Microstructure of cycle 1, cycle 4 and cycle 8 investigated by TEM images. By analyzing TEM images the grain size measured below 100 nm in cycle 8 and it was with an average grain size of 200 nm. Corrosion resistance of rolled copper strips in comparing with unrolled copper strip was investigated in acidic (pH=2) 3.5 wt. % NaCl solution. Potentiodynamic polarization and EIS tests used for corrosion resistance investigations. The corrosion morphologies analyzed by FE-SEM microscopy after polarization test and immersion for 40 hours. Results show that the corrosion resistance decreased up to cycle 2 and increased after rolled for forth time. The corrosion degradation was more intergranular in cycle 2 and unrolled counterpart. It was more uniform rather than intergranular type in cycle 8. Corrosion current density in unrolled sample (2.55 µAcm -2 ) was about two times of that in cycle 8 (1.45 µAcm -2 ). The higher corrosion rate in cycle 2 in comparison with others was attributed to unstable microstructure and increase in dislocation density whereas the uniform corrosion in cycle 8 was due to stable UFG formation

---

In this paper, gold leaching of a refractory sulfide concentrate by chloride–hypochlorite solution was investigated and effects of stirring speed, temperature and particle size on the leaching rate were reported. Experimental data for leaching rate of gold were analyzed with the shrinking–core model. Results were consistent with chemical reaction control mechanism in the first 1 h of leaching and diffusion control mechanism in the second 1 h. Apparent activation energy also was found to be 22.68 kJ/mol in the first step and 3.93 kJ/mol in the second step of leaching.

---

Geometrical design of the spiral crystal selector can affect crystal orientation in the final single crystal structure. To achieve a better understanding of conditions associated with the onset of crystal orientation in a spiral crystal selector, temperature field was investigated using three-dimensional finite element method during the process. Different geometries of spiral crystal selector were used to produce Al- 3 wt. % Cu alloy single crystal using a Bridgman type furnace. The Crystal orientation of the samples was determined using electron backscattered diffraction (EBSD) and optical microscopy. Analysing the temperature field in the crystal selector revealed that, the orientation of growing dendrites against liquidus isotherm in the spiral selector was the reason for crystal misorientation which differs in various selector geometries. Increasing the take-off angle from 35° up to 45° increases the misorientation with respect to <001> direction. Further increase of take-off angle greater than 45° will decrease the crystal misorientation again and the efficiency of the selector to produce a single grain is decreased.

---

In this study, effect of immersion time on the electrochemical behaviour of AISI 321 stainless steel (AISI 321) in 0.1 M H 2SO 4 solution under open circuit potential (OCP) conditions was evaluated by potentiodynamic polarization, Mott–Schottky analysis and electrochemical impedance spectroscopy (EIS). Mott–Schottky analysis revealed that the passive films behave as n-type and p-type semiconductors at potentials below and above the flat band potential, respectively. Also, Mott–Schottky analysis indicated that the donor and acceptor densities are in the range 1021 cm-3 and increased with the immersion time. EIS results showed that the best equivalent circuit presents two time constants: The high-medium frequencies time constant can be correlated with the charge transfer process and the low frequencies time constant has been associated with the redox processes taking place in the surface film. According to this equivalent circuit, the polarization resistance (interfacial impedance) initially increases with the immersion time (1 to 12 h), and then it is observed to decreases. This variation is fully accordance with potentiodynamic polarization results

---

The conical nanostructure improves the applications of alumina membranes and provides three dimensional nanometer scale systems to study the chemical and physical properties. In this study, the nano cone structure is produced in porous anodic alumina (PAA) by two-step anodizing. This conical nanostructure will improve the application of PAA membranes. This approach is novel generation of the so-called "gradually decreased voltage" technique, in which the voltage- time curve is divided into three stages and the effect of each step is investigated for different electrolytes. The effect of the decreasing voltage is examined in two types of electrolytes oxalic and phosphoric acid with a constant decrease in voltage rate. The results of SEM, FE-SEM images show the slope of the inner cone layer in the oxalic acid to be considerably larger compared with phosphoric acid.

---

High quality GGG:Cr,Ca crystal for passive Q-switching Nd:garnet lasers has been grown by the Czochralski method. Thermal treatment of GGG crystals co-doped with Cr4+ and Ca2+ at different temperatures is investigated. The absorption spectra were resolved into different peaks, of modified Gaussian line-shape. Transition from octahedral sites to tetrahedral ones is thermally activated. An optimal temperature interval for this transition was found to be 1200-1300 ˚C. The investigated samples were used as saturable absorbers in flash-lamp pumped Nd:YAG laser, and a pulse width of about 16 nsec was obtained

---

The effect of titanium dioxide addition on bonding strength of CaO-P2O5 -Na 2O-TiO2glass-ceramic system was investigated as a coating on titanium substrate. Thus, different amounts of TiO2 (2, 3.5 and 5mol %) were added to the base glass batch composition. The prepared glaze slips were applied on the substrate by dip coating method, dried and then heat treated at various temperatures. After that, bonding strength of the glass- substrates was determined via shear stress testing method. The de-bonded interfaces were analyzed by scanning electron microscopy (SEM). According to these results, the 5 mol% TiO 2 containing coating showed the best bonding strength, comparing with the other coatings. The bioactivity of the coated samples was investigated by soaking them in simulated body fluid (SBF). The surface of the samples was studied using SEM and X-Ray microprobe and it was observed that an apatite layer was grown on their surface

---

In this research, infiltration behavior of W-Ag composite compacts with Nickel and Cobalt as additives has been investigated. Nickel and Cobalt were added to Tungsten powder by two distinct methods: mixing elementally and reduction of salt solution. The coated Tungsten powders were compacted under controlled pressures to make porous skeleton with 32-37 vol. % porosity. Infiltration process was carried out at 1100 ̊C under a reducing atmosphere for 1h. The effect of additives on infiltration of Ag and density were evaluated by SEM and Archimedes methods. Properties of the specimens were compared following two distinct processes namely: I) sintering simultaneously with infiltration process and II) sintering prior to infiltration (pre-sintering process). It was found that specimens which were pre-sintered and then infiltrated with molten silver represent higher hardness and finer microstructure than the specimens infiltrated simultaneously with sintering.

---

Metallic-intermetallic laminate (MIL) composites are promising materials for structural applications especially in the aerospace industry. One of the interesting laminate composites is the Ti-TiAl 3 multilayer. In this work, commercially pure sheets of aluminum and titanium with almost equal thickness of around 0.5 mm were explosively joined. The achieved multilayers were annealed at 630 ℃in different times so that an intermetallic layer was formed at the Ti/Al interface. The resulting microstructure was studied by optical and scanning electron microscopy and Energy Dispersive Spectroscopy (EDS). TiAl3 was the only intermetallic phase that was observed in all annealing times. The kinetics of the formation of TiAl 3 was investigated and compared to previous research studies performed on Ti-Al multilayers which were fabricated using methods other than explosive welding.

---

Four compositions of austenitic Mn-Cr steels have been developed successfully for in-vessel component materials in power plant industry. The phase stability of these Mn-Cr steels was studied by and X-ray diffraction (XRD) patterns. XRD patterns have shown that the matrix of these Mn-Cr steels is a single γ-phase structure. The potentiodynamic polarisation curves suggested that these fabricated Mn-Cr steels showed passive behaviour in 0.1M H2SO 4solution. Therefore, semiconducting behaviour of passive film formed on these fabricated Mn-Cr steels in 0.1M H2SO 4 solution was evaluated by Mott–Schottky analysis. This analysis revealed that passive films behave as n-type and p-type semiconductors. Based on the Mott–Schottky analysis, it was also shown that donor and acceptor densities are in the order of 1021 cm -3 and are comparable for other austenitic stainless steels in acidic environments

---

Achieving extreme hardness in the newly synthetic steel formed by converting from initial amorphous state to subse-quent crystalline structure –named as devitrification process- was studied in this research work. Results of TEM observa-tions and XRD tests showed that crystallized microstructure were made up four different nano-scale phases i.e., α-Fe, Fe 36 Cr12 Mo10 , Fe 3 C and Fe3 B. More, Vickers hardness testing revealed a maximum hardness of 18.6 GPa which is signifi-cantly harder than existing hardmetals. Detailed kinetic and structural studies have been proof that two key factors were contributed to achieve this extreme hardness supersaturation of transition metal alloying elements (especially Nb) and also reduction in the structure to the nano-size crystals.

---

B4C and its composites with TiB2 as second phase continues to be extensively used as the preferred ceramic material in military applications as armor systems for absorbing and dissipating kinetic energy from high velocity projectiles. It also exhibits a high melting point (2427 °C), and high neutron absorption cross section. Pressureless sintering of the B 4C-nanoTiB2 nanocomposite using small amount of Fe and Ni (≤3 Wt%) as sintering aids was investigated in order to clarify the role of Fe and Ni additions on the mechanical and microstructural properties of B4C-nanoTiB2 nanocomposites. Different amount of Fe and Ni, mainly 1 to 3 Wt% were added to the base material. Pressureless sintering was conducted at 2175, 2225 and 2300 °C. It was found that Addition of 3 Wt% Fe and 3 wt% Ni and sintering at 2300 °C resulted in improving the density of the samples to about 99% of theoretical density. The nanocomposite samples exhibited high density, hardness, and microstructural uniformity.